Plasting molding and method and apparatus for producing the same by injection molding

ABSTRACT

A plastic molding for use in an optical device, a method of producing the molding by injection molding, and an apparatus for practicing the method are disclosed. Only a part of a molding expected to sink is surely caused to sink while, e.g., a mirror surface is surely transferred to a desired part of the molding.

This application is a division of application Ser. No. 09/053,050 field Apr. 1, 1998 now U.S. Pat. No. 6,287,504.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a lens, mirror, prism, or similar plastic molded article or product produced by injection molding and included in an optical device, e.g., a copier, laser printer, facsimile apparatus, or similar image forming apparatus, and a method and apparatus for producing the same. More particularly, the present invention is concerned with a plastic molded article or product having, e.g., mirror surfaces and a fine undulation pattern transferred thereto with high accuracy by injection molding, and a method and apparatus for producing the same.

2. Discussion of Background

For injection molding, it is a common practice to use a mold assembly including an inner mold surface forming a cavity having a preselected volume, a transfer surface formed on the inner mold surface for transferring a mirror surface to a molded article or product, and a gate or sprue open at the inner mold surface and having a preselected opening area. Molten resin is injected into the cavity via the gate or sprue and then cooled. The resulting molded article or product is taken out by opening the mold assembly. While such a molded article or product, particularly a mirror, lens, prism, or similar optical element, is required to have an accurate mirror surface and a uniform refractive index, the mirror surface needing a high surface accuracy is caused to sink because the molten resin contracts at the time of solidification.

Injecting molding methods for solving the above-described problem are taught in, e.g., Japanese Patent Laid-Open Publication Nos. 3-128218, 8-234005, 3-151218, and 3-281213 (hereinafter “Prior Art 1”). In Prior Art 1, either a non-transfer surface, or a mold surface which faces a transfer surface, is formed with, e.g., a roughened mirror surface or a surface treated so as to have a lower wettability, or else use is made of a porous material. Injection is stopped just before a cavity is filled up with molten resin. Then, the molten resin is solidified by cooling without any dwelling. As a result, the roughened surface is caused to sink due to a difference in adhering force between the molten resin, the transfer surface, and the roughened surface. This prevents the mirror surface of the molded article or product from sinking. Alternatively, an overflow portion for receiving excess molten resin is located outside of the cavity. When the overflow portion begins to be filled, injection is stopped. Then, the molten resin is solidified by cooling without any dwelling. This also allows the roughened surface to sink due to a difference in adhering force between the resin, the transfer surface, and the roughened surface.

An injection molding method disclosed in Japanese Patent Laid-Open Publication No. 2-175115 (hereinafter “Prior Art 2”) injects molten resin into a cavity in which a porous member, which communicates with a compressed gas such as air, is provided on an inner mold surface so as to contact the non-transfer surface of a molded article or product. While dwelling and cooling are under way after the injection of the molten resin, air is fed to the non-transfer surface of the molded article or product via the porous member. With this method, a side of a cylindrical thin lens (i.e., the molded article or product) may be caused to sink.

Japanese Patent Laid-Open Publication No. 6-304973 (hereinafter “Prior Art 3”) proposes an injection molding method in which a non-transfer surface communicates with the outside air via a vent hole. During an interval between the beginning and the end of the injection of molten resin into a cavity, a pressure difference is generated between the transfer surface and the non-transfer surface of the resin. As a result, the non-transfer surface of the resin is caused to sink. Specifically, air is brought into contact with the molten resin, on a surface other than the mirror surface of the molded article or product transferred from the transfer surface of the mold assembly, via the vent hole and a bore communicating therewith, so that the cooling speed of the molten resin is lowered. At the same time, a preselected air pressure is fed to the vent hole in order to generate a preselected pressure difference between the mirror surface of the molded article or product and the vent hole. This allows only the portion of the resin facing the vent hole to sink, i.e., prevents the mirror surface of the molded article or product from sinking. In addition, because only the portion of the resin facing the vent hole sinks, a molded article or product can be produced by simple control over the amount of the molten resin to be injected into the cavity and without any strain being generated in the resin. The resulting molded article or product is therefore free from an internal strain and is provided with an accurate mirror surface.

Prior Art 3 further teaches that the vent hole may communicate with a compressor so as to apply a preselected air pressure to the portion of the resin facing the vent hole. With this configuration, it is possible to generate any desired pressure difference between the mirror surface of the molded article or product and the portion of the resin facing the vent hole, thereby causing the portion of the resin facing the vent hole to sink. In addition, the pressure difference is readily adjustable in order to further enhance the accuracy of the mirror surface without any internal strain.

Japanese Patent Laid-Open Publication No. 6-315961 (hereinafter “Prior Art 4”) teaches an injection molding method causing the non-transfer surface of resin to sink. In accordance with this method, the transfer surface of a mold assembly is heated to and held at a high temperature. The transfer surface side of the resin is heated to a high temperature until the injection of molten resin into a cavity ends.

However, the above-described injection molding methods of Prior Art 1, Prior Art 2, Prior Art 3, and Prior Art 4 have some drawbacks. More particularly, Prior Art 1, which relies on any one of the roughened surface, surface treatment, or porous material, results in an expensive mold assembly. Moreover, stopping the injection just before the cavity is filled up with the molten resin is extremely difficult. Should the correct timing for stopping the injection of molten resin not be realized, the relationship in the adhering forces between the transfer surface and the roughened surface would be inverted and would thereby cause the mirror surface of the molded article or product to sink or else result in a shortage of resin. In addition, because sinking cannot be provided with directionality and because setting the molding conditions is difficult, the configuration of the molded article or product is critically limited. It is more preferable that the injection of the molten resin be stoppable at any time within a broader range of times. However, in this case, the overflow portion, which is formed integrally with the molded article or product, must be removed by an extra step. Moreover, if the area of the opening of the gate or sprue for feeding the molten resin to the overflow portion is excessively small, the relationship in adhering force between the transfer surface and the roughened surface would also be inverted and would thereby cause the mirror surface of the molded article or product to sink. Also, there would not be enough of the molten resin.

Prior Art 1 can be implemented as a mirror or similar optical element needing a single mirror surface, because it roughens the mold surface facing the transfer surface. However, Prior Art 1 cannot produce a lens, prism, or similar optical element, because the number and positions of the mirror surfaces are limited. In addition, the relationship in adhering force is inverted and causes the mirror surface of the molded article or product to sink, depending on the material constituting the transfer surface and roughened surface and the kind of resin used.

Prior Art 2 increases the cost of the mold assembly due to the porous member and provides more sophisticated control over the configuration of the porous member. Specifically, if the effect of the porous member is excessive, it not only admits the molten molding material thereinto, by also obstructs the parting of the molded article or product from the mold assembly. This is particularly true when the porous portion of the porous member extends inwardly over the wall of the mold assembly. Further, because the compressed gas is fed to the non-transfer surface of the molded article or product via the porous member during the previously stated interval, a pressure difference is maintained between the non-transfer surface and the transfer surface of the molten resin during cooling. As a result, the internal strain remains in the resulting molded article or product after the opening of the mold assembly. The residual pressure not only lowers the accuracy of the transfer surface, but also causes the entire molded article or product to deform.

Prior Art 3 generates a pressure difference between the transfer surface and the non-transfer surface of the resin during the interval mentioned earlier. This also brings about the problem stated above in relation to Prior Art 2. Prior Art 4 maintains the transfer surface of the mold assembly at high temperature and heats the transfer surface side of the resin to a high temperature during the previously mentioned interval. This is also undesirable in the above-described respect.

SUMMARY OF THE INVENTION

It is therefore an object of the present invention to provide a plastic molded article or product, wherein only a desired portion thereof sinks, wherein a mirror surface is provided in another desired portion thereof, and wherein a method and an apparatus for producing the same by injection molding are further provided.

It is another object of the present invention to provide an inexpensive and least deformable plastic molded article or product, wherein only a non-transfer surface thereof sinks so that the molded article or product has a highly accurate transfer surface.

In accordance with the present invention, in a molded article or product produced by an injection mold assembly having a pair of molds including an inner mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface to the molded article or product from the inner mold surface, and a gate or sprue for filling the cavity with a molten molding material by injection, and by injecting the molten molding material into the cavity via the gate or sprue and then cooling the molten molding material, the injection mold assembly includes at least one vent hole having a preselected opening area, and at least one bore communicating with the vent hole for applying a preselected air pressure to the molded article or product. A step portion is formed on the inner mold surface between the vent hole and the transfer surface.

Also, in accordance with the present invention, in an injection molding method for producing a molded article or product by using a mold assembly having a pair of molds including an inner mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface to the molded article or product from the inner mold surface, and a gate or sprue for filling the cavity with a molten molding material by injection, and by injecting the molten molding material into the cavity via the gate or sprue and then cooling the molten molding material, the inner mold surface is formed with, outside of the transfer surface, with at least one vent hole having a preselected opening area and at least one bore communicating with the vent hole for applying a preselected air pressure to the molten molding material. The air pressure is continuously generated via the vent hole even after the pressure of the molten molding material in the cavity has dropped to zero.

Further, in accordance with the present invention, a mold assembly has a pair of molds including an inner mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface to a molded article or product from the inner mold surface of the mold assembly, and a gate or sprue for filling the cavity with a molten molding material by injection, and injects the molten molding material into the cavity via the gate or sprue and then cools the molten molding material. The inner mold surface is formed with, outside of the transfer surface, at least one vent hole having a preselected opening area and at least one bore communicating with the vent hole for applying a preselected air pressure to the molten molding material, and at least one exhaust hole located at a position adjoining the vent hole, but not facing the transfer surface.

Moreover, in accordance with the present invention, a method of producing a plastic molded article or product begins with the step of preparing a mold assembly including at least one transfer surface and at least one non-transfer surface formed on a surface other than the transfer surface. The transfer surface and non-transfer surface forms at least one cavity. Molten resin, heated to a temperature above a softening point thereof, is injected into the cavity. A resin pressure is caused to act on the transfer surface to thereby cause the molten resin to adhere to the transfer surface, and then the molten resin is cooled to a temperature below the softening point. The mold assembly is opened in order to allow the resulting molded article or product to be taken out. The temperature of at least one non-transfer surface of the resin is lowered below the temperature of the resin on the transfer surface during an interval between the beginning and the end of injection of the molten resin into the cavity.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, features and advantages of the present invention will become more apparent from the following detailed description taken with the accompanying drawings in which:

FIG. 1 is a fragmentary view showing a conventional injection mold assembly;

FIG. 2 is a plan view showing a specific vent hole formed in the inner mold surface of a sink insert included in the mold assembly of FIG. 1;

FIG. 3A is a perspective view showing a specific molded article or product produced by the mold assembly of FIG. 1;

FIG. 3B is a side elevational view of the molded article or product of FIG. 3A;

FIG. 3C is a cross-sectional view taken along line 3 c-3 c of FIG. 3B;

FIG. 4A is a side elevational view showing a specific molded article or product produced by injection molding with an air stream flowing toward the reference surface of a cavity;

FIG. 4B is a cross-sectional view taken along line A of FIG. 4A;

FIG. 5A is a top plan view showing a specific molded article or product produced by injection molding and caused to sink as far as its mirror surface portion;

FIG. 5B is a side elevational view of the molded article or product shown in FIG. 5A;

FIG. 5C is a cross-sectional view taken along line A of FIG. 5B;

FIG. 6 shows a relationship between the molded article or product produced by the mold assembly of FIG. 1 and the position of a vent hole;

FIG. 7A is a perspective view showing a molded article or product and an injection mold assembly representative of a first embodiment of the present invention;

FIG. 7B is a fragmentary cross-sectional view of the mold assembly shown in FIG. 7A;

FIG. 8 is a perspective view of a molded article or product representative of a second embodiment of the present invention;

FIG. 9A is a perspective view of a molded article or product representative of the third embodiment of the present invention;

FIG. 9B is a cross-sectional view of the third embodiment in plane A1 of FIG. 9A;

FIG. 9C is a cross-sectional view of the third embodiment in plane A2 of FIG. 9A;

FIGS. 10A and 10B are cross-sectional views of a molded article or product each showing a particular configuration of steps included in the third embodiment, wherein FIG. 10A shows steps protruding from the sink surface of the molded article or product and FIG. 10B shows steps extending into the sink surface of the molded article or product;

FIG. 11A is a perspective view of a molded article or product representative of a fourth embodiment of the present invention;

FIG. 11B is a cross-sectional view taken along plane A of FIG. 11A;

FIG. 12A is a perspective view of a molded article or product representative of a fifth embodiment of the present invention;

FIG. 12B is a cross-sectional view taken along plane A of FIG. 12A;

FIG. 13A is a perspective view of a molded article or product representative of a sixth embodiment of the present invention;

FIG. 13B is a cross-sectional view taken along plane A of FIG. 13A;

FIG. 14A is a perspective view of a molded article or product representative of a seventh embodiment of the present invention;

FIG. 14B is a cross-sectional view taken along plane A of FIG. 14A;

FIG. 15 is a cross-sectional view of a molded article or product representative of an eighth embodiment of the present invention and including tapered steps;

FIGS. 16A and 16B are cross-sectional views each showing a particular configuration of a molded article or product representative of a ninth embodiment of the present invention;

FIGS. 17A and 17B are graphs showing the variation of the internal pressure of molten resin existing in a cavity occurring from the beginning to the end of cooling of the molten resin, and a timing for switching an air pressure fed via a vent hole, respectively;

FIG. 18 is a cross-sectional view of an injection mold assembly representative of an eleventh embodiment of the present invention;

FIG. 19 is a perspective view showing a positional relationship between a vent hole and an exhaust hole included in the eleventh embodiment;

FIG. 20 is a cross-sectional view of an injection mold assembly representative of a twelfth embodiment of the present invention;

FIG. 21 is a perspective view showing the position of an exhaust hole formed in an injection mold assembly representative of a thirteenth embodiment of the present invention;

FIG. 22 is a perspective view showing a modification of the thirteenth embodiment;

FIG. 23A is a perspective view of a plastic molded article or product representative of a fifteenth embodiment of the present invention;

FIG. 23B is a side elevation showing a sinking region to occur in the fifteenth embodiment;

FIG. 23C is a cross-sectional view taken along line A—A of FIG. 23B;

FIG. 24A is a cross-sectional view showing one half of the fifteenth embodiment;

FIG. 24B is a perspective view showing cavity inserts included in the fifteenth embodiment;

FIG. 25A is a cross-sectional view as seen in a direction X of FIG. 24B;

FIG. 25B is a cross-sectional view as seen in a direction Y of FIG. 24B;

FIG. 26 is a cross-sectional view showing a method and an apparatus for producing a plastic molded article or product representative of a sixteenth embodiment of the present invention;

FIGS. 27A-27D show a specific procedure available with the sixteenth embodiment;

FIGS. 28A-28D show another specific procedure available with the sixteenth embodiment;

FIG. 29 is a top plan view showing a method and an apparatus for producing a plastic molded article or product representative of a seventeenth embodiment of the present invention;

FIGS. 30A and 30B show another specific procedure available with the seventeenth embodiment;

FIG. 31 is a top plan view showing a method and an apparatus for producing a plastic molded article or product representative of an eighteenth embodiment of the present invention;

FIG. 32A is a perspective view showing mirror, reference, and sink inserts included in the eighteenth embodiment;

FIG. 32B is a cross-sectional view as seen in a direction X of FIG. 32A;

FIG. 32C is a cross-sectional view as seen in a direction Y of FIG. 32A;

FIGS. 33A and 33B show another specific procedure available with the eighteenth embodiment;

FIGS. 34A-34C show a procedure following the procedure of FIG. 32B; and

FIG. 35 shows a modification of the eighteenth embodiment.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

To better understand the present invention, brief reference will be made to the injection molding method taught in Prior Art 3 mentioned earlier. As shown in FIG. 1, a mold assembly 10 is made up of a stationary or upper mold 11 and a movable or lower mold 12, a pair of mirror pieces or inserts 13 and 14, a reference insert 15, and a sink insert 16 together forming a cavity 17 having a preselected volume. Each of the mirror pieces or inserts 13 and 14 has a transfer or mold surface 13 a and 14 a, respectively, for transferring a mirror surface 22 and 23 to a molded article or product 21 (see FIG. 3A). The reference insert 15 has a mold surface or transfer surface 15 a for transferring a reference surface or C surface 25 to a molded article or product 21 (see FIG. 3A). The sink insert 16 has a mold surface or a sink surface 16 a for causing a sink surface or B surface of a molded article or product 21 (see FIG. 3A) to sink. Molten resin or similar molten molding material 20 is injected into the cavity 17 via a gate or sprue (not shown) similar to the one (i.e., gate or sprue 63) shown in FIGS. 25B, 27A-D, 30A-B, 32C, 33A-B, and 34A-C. The mold surface or sink surface 16 a of the sink insert 16 is formed with a vent hole 18 having a preselected opening area, and a bore communicating with the vent hole 18. Air 9, under preselected pressure, is fed to the molten resin or molten molding material 20 via the bore 19 and vent hole 18.

FIG. 2 shows a specific configuration of the vent holes 18 formed in the sink inset 16 and extending to the mold surface 16 a. To feed air to the molten molding material 20, use may be made of natural draft utilizing a pressure difference between the mirror portion of the molten molding material 20 and the vent hole portion, or forced draft generating a desired pressure difference between the two portions with a compressor (not shown) communicating with the vent hole 18.

In the mold assembly 10, the vent hole 18 is positioned at the side of a molded article or product which is expected to sink. When air 9 is fed to the cavity 17 via the bore 19 and vent hole 18, sinking successfully occurs in the expected surface (i.e., sink surface 24) of the molded article or product. In addition, the transfer surfaces 13 a and 14 a of the mirror pieces or inserts 13 and 14, respectively, are desirably transferred to the molded article or product. The molded article or product therefore suffers from a minimum of internal strain.

A specific molded article or product 21, produced by the mold assembly 10, is shown in FIGS. 3A-3C. As shown, the molded article or product is implemented as a rectangular lens having mirror surfaces (optical surfaces) 22 and 23 transferred from the transfer surfaces 13 a and 14 a, respectively, of the mirror pieces or inserts 13 and 14, respectively. FIG. 3B shows the surface 24 of the lens 21 intended to sink (i.e., sink surface or B surface). A sinking area (or sunken area) 24 a is indicated by cross-hatching. As shown, desired sinking occurs on the sink surface or B surface 24 of the molded article or product 21 (i.e., lens). As a result, the mirror surfaces 22 and 23 are desirably transferred to the molded article or product 21 (i.e., lens), reducing the internal strain of the molded article or product 21 (i.e., lens).

However, the injection mold assembly 10 has the following problems left unsolved. If the various mold parts, namely, the stationary or upper mold 11, the movable or lower mold 12, the upper mirror insert 13, the lower mirror insert 14, the reference insert 15, and the sink insert 16, constituting the mold assembly 10, lack in accuracy, either individually or in combination, a gap d is formed between the parts, as shown in FIG. 1. Then, air 9 is likely to flow into the cavity 17 via the gap d and prevent the desired surface from sinking. FIGS. 4A and 4B are views similar to FIGS. 3A and 3B, showing a molded article or product 21 (i.e., lens) molded with a stream of air 8 (see left side of FIG. 1) flowing into the side of the mold assembly 10 adjacent to the surface 15 a of the reference insert 15 of the cavity 17 and against the C surface 25 of the molded article or product 21. As shown, the molded article or product 21 (i.e., lens) fails to sink to a desired degree or practically fails to sink at its expected surface (i.e., sink surface or B surface 24). In the worst case scenario as shown in FIGS. 4A and 4B, a C surface 25 is caused to sink (see sunken area 25 a) and the surface 15 a of the reference insert 15 of the mold assembly 10 loses surface accuracy as a transfer surface.

Further, when air 9 is introduced into the cavity 17 via the vent hole 18 by either natural draft or forced draft, it is apt to reach the mirror surfaces 22 and 23 and cause them to sink also, depending on the amount of molten resin 20 filled in the cavity 17 or the amount of air 9. A molded article or product 21 (i.e., lens) caused to sink as far as its mirror surfaces 22 and 23 is shown in a top plan view in FIG. 5A, in a side elevational view in FIG. 5B, and in a cross-sectional view, taken along line 5 c-5 c of FIG. 5B, in FIG. 5C. As shown, a sunken region 24 a formed in the sink surface or B surface 24 extends even to the mirror surface 22 and introduces a strain in the mirror surface 22, thereby deteriorating the ability of the molded article or product 21 (i.e., lens).

Preferred embodiments of the present invention will be described hereinafter.

FIG. 6 is a prior art figure showing the positional relationship between the conventional molded article or product 21 and the vent hole 18 of the mold assembly 10. The relationship shown in FIG. 6 brings out the problem discussed with reference to FIGS. 5A-5C. A first embodiment of the present invention eliminates such a problem by providing a molding with steps 26 between a vent hole 18 and transfer surfaces 13 a and 14 a of the mirror inserts 13 and 14, respectively.

First Embodiment

Specifically, FIG. 7A shows a specific molded article or product 21 representative of the first embodiment. FIG. 7B is a partial cross-sectional view of an injection mold assembly 10 for producing the molded article or product 21. Basically, the mold assembly 10 is similar to the conventional mold assembly 10 shown in FIG. 1, and has its structural elements designated by the same reference numerals. The difference is that, as shown in FIG. 7B, the mold assembly 10 of the first embodiment includes a cavity 17 and indentations 6 formed in a sink insert 16 between a vent hole 18 and transfer surfaces 13 a and 14 a of the mirror inserts 13 and 14, respectively, wherein the indentations 6 are for forming steps 26 on the molded article or product 21.

More specifically, the molded article or product 21 is implemented as a rectangular lens having two mirror surfaces (optical surfaces) 22 and 23 playing the role of lens surfaces. The molded article or product 21 (i.e., lens) includes a surface 24 that will be allowed to sink (i.e., sink surface or B surface). The steps 26 are formed on the surface 24 between 22 and 23 from the vent hole 18.

As shown in FIG. 7B, the sink insert 16 of the mold assembly 10 includes the indentations 6 complementary in configuration to the steps 26 of the molded article or product 21 (i.e., lens) and formed on the mold surface, respectively. Just after the molten resin or molten molding material 20 has been injected into the cavity 17 (between mirror inserts 13 and 14, reference insert 15, and sink insert 16), air 9 is forced out of the cavity 17 via the vent hole 18 and a bore 19 due to the high internal pressure of the molten resin 20. The internal pressure of the molten resin 20 sequentially decreases as the molten resin 20 is cooled. When the pressure of the molten resin 20 decreases below the atmospheric pressure or below a compression pressure (i.e., when a compressor communicates with the vent hole 18 via the bore 19), air 9 begins to flow into the cavity 17 via the vent hole 18, causing the molten resin 20 to sink away from the vent hole 18. If the molten resin 20 did not include the steps 26, the molten resin 20 might sink as far as the transfer surfaces 13 a and 14 a of the mirror inserts 13 and 14, respectively. In the illustrative embodiment, the steps 26, which isolate the mirror surfaces 22 and 23 from the vent hole 18, tend to contract toward each other, as indicated by the arrows in FIG. 7B. However, the indentations 6 of the sink insert 16 of the mold assembly 10 interfere with the steps 26 and prevent the steps 26 from contracting. As a result, the molten resin 20 and mold assembly 10 remain in close contact with each other and prevent sinking from proceeding over the steps 26 (i.e., confine the sinking to the region between the steps 26). The molded article or product 21 (i.e., lens) is therefore caused to sink only 22 and 23 by means of a transfer mechanism.

Second Embodiment

FIG. 8 shows a molded article or product 21 representative of a second embodiment of the present invention and produce by injection molding. The molded article or product 21 is also implemented as a lens similar in configuration to the lens of FIG. 7A. As shown, a step 26 is formed on the sink surface or B surface 24 of the molded article or product 21 (i.e., lens) adjoining the vent hole (not shown) such that the step 26 surrounds the vent hole (not shown). The step 26 surrounding the vent hole (not shown) prevents air 9 from turning around and allows the sinking region to be controlled more positively than in the first embodiment.

Third Embodiment

FIGS. 9A-9C show a molded article or product 21 representative of a third embodiment of the present invention. The molded article or product 21 is also implemented as a lens similar in configuration to the lens of FIG. 7A. As shown, a step 26 is formed on the sink surface or B surface 24 of the molded article or product 21 adjoining the vent hole (not shown). The top portion of the step 26 has a substantially similar contour as the contour of the upper portion of the sink surface or B surface 24. Specifically, when the molded article or product 21 is a rectangular lens, the step 26 surrounds the vent hole (not shown) and has an upper portion with a contour similar to the contour of the upper portion of the sink surface or B surface 24 of the molded article or product 21 (i.e., lens). The degree of sinking of a sunken region 24 a can therefore be controlled in a ratio similar to the cross-sectional area of each cross-section of the molded article or product 21 (see section A1 or A2 as shown in FIGS. 9A, 9B, and 9 c). This successfully makes the internal strain and surface accuracy uniform and thereby enhances the accuracy of the molded article or product 21 (i.e., lens).

As shown in FIG. 10A, the steps 26, of the first to third embodiments, are each represented by projections extending outwardly from the sink surface or B surface 24 of the molded article or product 21 (i.e., lens). Alternatively, as shown in FIG. 10B, the steps 26 may be represented by recesses formed in the extending into the sink surface or B surface 24 of the molded article or product 21 (i.e., lens). The steps 26 implemented as recesses are for controlling the sinking region 24 a. When the steps 26 are recesses, as shown in FIG. 10B, the mold assembly 10 will be formed with outwardly extending projections around the vent hole 18 (instead of inwardly extending projections as shown in FIG. 7B).

Fourth Embodiment

FIGS. 11A and 11B show a molded article or product 21 representative of a fourth embodiment of the present invention. As shown, steps 26 are formed on the mirror surfaces 22 and 23 of the molded article or product 21. This configuration prevents air 9 from reaching the mirror surfaces 22 and 23 via the vent hole (not shown) because the steps 26 of the molded article or product 21 and the indentations 6 of the mold assembly (not shown) remain in close contact with each other.

Fifth Embodiment

FIGS. 12A and 12B show a molded article or product 21 representative of a fifth embodiment of the present invention. As shown, a step 26 is formed on a part of a mirror surface 22 or 23. Specifically, when it is known that air 9 will turn around to a part of the mirror surface 22 or 23 molded article or product 21 and cause it to sink beforehand, the step 26 may be formed only in such a part of the mirror surface 22 or 23. This configuration saves cost when a mold assembly (not shown) is formed with an indentation 6.

Sixth Embodiment

FIG. 13A shows a molded article or product 21 representative of a sixth embodiment of the present invention. FIG. 13B is a cross-sectional view taken along plane 13 b—13 b—13 b of FIG. 13A. As shown, steps 26 are formed on opposite edges of the mirror surface 22 contiguous with the sink surface or B surface 24 and C surface 25. Likewise, steps 26 are formed on opposite edges of the other mirror surface 23 contiguous with the sink surface or B surface 24 and C surface 25. As shown in FIG. 1, when the mold assembly 10 is not accurate, air is apt to enter the cavity 17 via an unexpected portion. As a result, as shown in FIGS. 14A and 14B specifically, air is likely to flow into the side of the cavity 17 of the mold assembly 10 adjacent to the reference surface 15 a of the reference insert 15 (i.e., C surface of the molded article or product 21) so that the air turns around to the mirror surfaces 22 and 23 to cause them to sink. In the illustrative embodiment, the steps 26 formed on both longitudinal edges of the mirror surface 22 and those of the mirror surface 23 prevent air from turning around to the mirror surfaces 22 and 23 and thereby prevents the mirror surfaces 22 and 23 from sinking.

Seventh Embodiment

FIG. 14A shows a molded article or product 21 representative of a seventh embodiment of the present invention. FIG. 14B is a cross-sectional view taken along plane 14 b—14 b—14 b of FIG. 14A. As shown, the molded article or product 21 is identical with the molded article or product 21 shown in FIG. 13A, except that the steps 26, facing each other of the mirror surfaces 22 and 23, are replaced with a single step 26 surrounding the mirror surface 22 or 23. The steps 26 can obstruct air 9 more positively and can therefore prevent the mirror surfaces 22 and 23 from sinking more positively.

Eighth Embodiment

To obstruct air 9 tending to reach the mirror surfaces 22 and 23 of the molded article or product 21, the steps 26, shown in FIG. 13B or 14B, suffice. FIG. 15 shows a molded article or product 21 configured to be easily separable from a mold assembly 10. As shown, the steps 26 are each of a height h extending from the mirror surfaces 22 and 23. With the steps 26, the molded article or product 21 can be easily separated from a mold assembly 10, while preserving its accuracy.

Ninth Embodiment

FIGS. 16A and 16B each shows a particular molded article or product 21 representative of a ninth embodiment of the present invention. As shown, steps 26, facing each other at both edges of each mirror surface 22 or 23, are provided with a triangular cross-section (FIG. 16A) or an accurate cross-section (FIG. 16B). This not only enhances the parting ability of the molded article or product 21, but also simplifies the procedure for forming indentations 6 in, e.g., the mirror pieces 13 and 14 of the mold assembly 10.

In each of the eighth and ninth embodiments, the steps 26 each have a height h greater than 0.1 mm inclusive. Experiments showed that heights h greater than 0.1 mm inclusive can sufficiently obstruct air.

Tenth Embodiment

This embodiment relates to a method of forming a molded article or product 21 and will be described with reference to FIG. 7B. First, the movable or lower mold 12, carrying the mirror piece or insert 14 and the reference insert 15 therewith, is brought into contact with the stationary or upper mold 11, loaded with the other mirror insert 13 and the reference insert 15. As a result, the mold surfaces of the molds 11 and 12 form the cavity 17 having a preselected volume. A gate or sprue (not shown) is formed in a mold surface (not shown) of the mold assembly 10 in order to inject the molten resin 20 into the cavity 17. A conventional filling machine (not shown) is connected to the gate or sprue in order to fill the cavity 17 with the molten resin 20 by injection.

Just after molten resin or molten molding material 20 has been injected into the cavity 17, air is forced out of the cavity 17 via the vent hole 18 and a bore 19 due to the high internal pressure of the molten resin 20. The internal pressure of the molten resin 20 decreases below the atmospheric pressure or below a compression pressure (i.e., when a compressor communicates with a vent hole 18 via a bore 19), air 9 begins to flow into the cavity 17 via the vent hole 18, causing the molten resin 20 to sink away from the vent hole 18. At this instant, the steps 26, isolating the mirror surfaces 22 and 23 from the vent hole 18, as shown in, e.g., FIG. 7A, tend to contract toward each other, as indicated by arrows in FIG. 7B. However, the indentations 6 of the mold assembly 10 interfere with the steps 26 and prevent them from contracting. As a result, the molten resin 20 and mold assembly 10 remain in close contact with each other and prevent sinking from proceeding over the steps 26.

FIG. 17 shows how the internal pressure of the molten resin 20 varies from the time when the molten resin 20 begins to be injected into the cavity 17 to the time when it is fully cooled off. In the case where air 9 under pressure is fed via the vent hole 18, its pressure is switched in a manner also shown in FIG. 17. As shown, in the illustrative embodiment, air 9 is continuously fed even after the internal pressure of the molten resin 20 has been lowered to zero, generating air pressure in the vent hole portion. Experiments showed that the air pressure continuously generated, even after the drop of the resin pressure to zero, allows the sinking region 24 a to be surely controlled.

More specifically, the molten resin 20 remains in close contact with the mold assembly 10 until the internal pressure of the molten resin 20 drops to zero, and sinking occurs thereafter. It is therefore necessary to apply air that has been pressured for some extra period of time after the internal pressure has dropped to zero. It was found that when the molded article or product 21 is a lens, as shown and described, the sinking region 24 a can be controlled if the air pressure is continuously applied for at least 5 seconds more after the drop of the internal pressure of the molten resin 20 to zero. The air pressure should preferably be higher than the atmospheric pressure (about 0.1 MPa) inclusive, but lower than 2 MPa inclusive.

The first to tenth embodiments, shown and described above, achieve the following various unprecedented advantages.

(1) In a molded article or product formed by an injection mold assembly, in which a pressure difference or an air pressure is generated between mirror surface portions corresponding to the mirror surfaces of a molten molding material or molten resin and a vent hole portion corresponding to a vent hole in order to cause the molten molding material or molten resin to sink, a step is formed in a cavity between the vent hole and a mirror surface portion. When the molten molding material or molten resin is cooled, the step prevents the resin from contracting over the step and thereby guarantees adhesion of the portions of the molding material other than a surface expected to sink and the mold assembly. This prevents sinking from proceeding over the step and thereby confines it to a region delimited by the step.

(2) The step is provided on the surface of the molded article or product facing the vent hole, so that the sinking region can be confined to such a surface.

(3) Two steps are formed in such a manner as to isolate the vent hole and the mirror surface portions, so that sinking is prevented from extending to the mirror surfaces.

(4) The step is formed to surround the vent hole in order to prevent air from turning around to the surface portions. This allows sinking to be confined to the region delimited by the step and thereby prevents sinking from extending to the mirror surfaces.

(5) When the step has a portion with a contour similar to the contour of the side of the molded article or product facing of the vent hole, the sinking region can be controlled in the same ratio as the cross-sectional area of the molded article or product. This makes the internal strain and surface accuracy of the molded article or product uniform and therefore enhances the accuracy of the molded article or product.

(6) The sinking region can be controlled both when the step or steps of the molded article or product are formed as projections and when they are formed as recesses.

(7) The step or steps prevent air from reaching the mirror surface portions via the vent hole and thereby protects the mirror surface portions from sinking.

(8) The steps configured to face each other at opposite longitudinal edges of each mirror surface obstruct air coming through the vent hole or any other portion of the mold assembly. This also surely protects the mirror portions from sinking.

(9) The steps are each configured to surround the associated mirror surface portion. This prevents air from reaching the mirror surfaces more positively and prevents the sinking of the mirror surface portions more positively.

(10) The steps are tapered in order to confine the sinking to the area delimited by the steps. In addition, the tapering of the steps enhances the parting ability of the molded article or product from the mold assembly.

(11) The steps are provided with a triangular or an arcuate cross-section in order to enhance the parting ability of the molded article or product from the mold assembly and to facilitate the formation of steps in the mold assembly.

(12) In a method of forming a molded article or product of the kind described, an air pressure is continuously generated via the vent hole even after the internal pressure of the molten resin in the cavity has dropped to zero so as to control the sinking region more positively.

Eleventh Embodiment

FIG. 18 shows an injection mold assembly 10 representative of an eleventh embodiment of the present invention. As shown, a sink insert 16 is located at a position where sinking is expected to occur. The sink insert 16 is formed with a vent hole 18, a bore 19 communicating with the vent hole 18, and a pair of exhaust holes 60 positioned above and below the vent hole 18 and the bore 19, respectively. FIG. 19 shows a positional relationship between the vent hole 18 and the exhaust holes 60.

In the illustrative embodiment, just after molten resin or molten molding material 20 has been injected into a cavity 17, it is difficult for air 9, fed under pressure via the vent hole 18, to enter the cavity 17. The internal pressure of the resin 20 sequentially decreases as the resin 20 is cooled. When the pressure of the molten resin 20 decreases below the pressure of the compressed air 9 delivered to the vent hole 18, the air 9 begins to flow into the cavity 17 via the vent hole 18. As a result, the portion of the molten resin 20 corresponding to one side (i.e., sink surface or B surface 24) of a molded article or product 21, as shown in FIG. 19, and facing the vent hole 18, begins to sink (see FIG. 18, X4 shows the distance of sinking) away from the inner periphery of the cavity 17. The compressed air 9, introduced into the cavity 17, hits against the molten resin 20 and then, is discharged from the cavity 17 via the exhaust holes 60. That is, the compressed air 9 is prevented from turning around to the upper mirror surface 22 and lower mirror surface 23 of the molded article or product 21. If desired, a machine for forced exhaustion may be connected to the bore 19 in order to promote discharge of the compressed air 9 more effectively. When the mold assembly 10 is used to form, e.g., a lens of resin applicable to an image forming apparatus or similar optical apparatus, the exhaust holes 60 should be 0.001 mm to 0.5 mm wide (vertical dimension in FIG. 18). With such a width, the exhaust holes 60 allow a minimum of resin to enter therein and thereby frees the molded article or product 21 from burrs.

Twelfth Embodiment

FIG. 20 shows a mold assembly 10 representative of a twelfth embodiment of the present invention. As shown, this embodiment is identical with the eleventh embodiment, except that the exhaust holes 60 are formed by porous member 61.

Thirteenth Embodiment

FIG. 21 shows the position of an exhaust hole 61 formed in an injection mold assembly 10 representative of a thirteenth embodiment of the present invention. As shown, a continuous exhaust hole 60 is formed to surround the vent hole 18. The exhaust hole 60 may also be formed by the porous member 61 in order to simplify the configuration of the sink insert 16, as shown in FIG. 20.

Fourteenth Embodiment

FIG. 22 shows a fourteenth embodiment of the present invention which is a modification of the thirteenth embodiment. As shown, this embodiment is identical with the thirteenth embodiment, except that an upper portion of an exhaust hole 60 has a similar contour to the contour of an upper portion of the side of the molded article or product 21 which is expected to sink (i.e., sink surface or B surface 24). Again, the exhaust hole 60 may be formed by the porous member 61 in order to simplify the configuration of the sink insert 16, as shown in FIG. 20.

The eleventh to the fourteenth embodiments, shown and described above, have the following unprecedented advantages.

(1) At least one exhaust hole is formed in the vicinity of a vent hole used to feed air under pressure for causing sinking. The exhaust hole discharges air, which causes sinking to occur in the vicinity of the vent hole, to the outside of a mold assembly before it reaches portions expected to form mirror surfaces. Therefore, air is prevented from reaching portions other than the portion expected to sink, so that the shape of the mold assembly is surely transferred to the other portions of the molding.

(2) A single exhaust hole surrounds the vent hole and discharges air, which causes sinking to occur smoothly, to the outside of the mold assembly. This guides air only to the portion of the molding expected to sink more positively.

(3) The exhaust hole or holes are formed by a porous member. Therefore, particularly when a single exhaust hole surrounds the vent hole, the porous member, formed with the holes, is simple in structure.

(4) Air is forcibly discharged via the exhaust holes so that air , which causes sinking to occur in the cavity, can be discharged more smoothly.

(5) The exhaust hole has an opening width as small as 0.001 mm to 0.5 mm and prevents a molding material from entering it. This frees the resulting molding from burrs.

Fifteenth Embodiment

FIGS. 23A-23C show a plastic molded article or product 21 formed by a method representative of a fifteenth embodiment of the present invention. The molded article or product 21 may be implemented, not only as a lens, but also as a mirror, prism or similar optical device. As shown, the molding molded article or product 21 has mirror surfaces 22 and 23 on its top and bottom, respectively. In addition, the molding molded article or product 21 has a reference surface or non-transfer surface or C surface 25 at one side and a sink surface or non-transfer surface or B surface 24 at the other side. The reference surface 25 is to be mounted to another part, while the sink surface 24 is expected to sink.

Reference will be made to FIGS. 24A, 24B, 25A, and 25B for describing a mold assembly 10 for producing the above molded article or product 21. As shown, the mold assembly 10 includes a stage 3 loaded with a movable or lower mold 12. A stationary or upper mold 11 is positioned above the movable or lower mold 12. The movable or lower mold 12 is movable into and out of contact with the stationary or upper mold 11 by being driven by a clamping device (not shown).

A plurality (four in the embodiment) of inserts, namely, mirror pieces or inserts 13 and 14, reference insert 15, and sink insert 16, are interposed between the movable or lower mold 12 and the stationary or upper mold 11 and constitute cavity inserts. Specifically, upper mirror piece or insert 13 and lower mirror piece or insert 14 face each other and are formed with transfer surfaces 13 a and 14 a, respectively, for forming the mirror surfaces 22 and 23, respectively, of the molded article or product 21. A reference insert 15 and a sink insert 16 face each other at both sides of the upper mirror piece or insert 13 and the lower mirror piece or insert 14 and are formed with non-transfer surfaces 15 a and 16 a, respectively, in order to form the reference surface or C surface 25 and sink surface or B surface 24, respectively. The surfaces 13 a, 14 a, 15 a, and 16 a of the upper mirror piece or insert 13, lower mirror piece or insert 14, reference insert 15, and sink insert 16 together form a cavity 17. The non-transfer surfaces 15 a and 16 a are each formed with fine irregularities or undulations 62.

It is noted that FIGS. 24A and 24B show only one half of the mold assembly 10. The other half is also provided with cavity inserts identical with the upper mirror piece or insert 13, lower mirror piece or insert 14, reference insert 15, and sink insert 16. A gate or sprue (not shown) is formed in the stationary or upper mold 11, while a gate or sprue 63 is formed in the upper mirror piece or insert 13 and is communicable to the gate or sprue (not shown) of the stationary or upper mold 11. An injection molding machine (not shown) feeds molten resin 20 to the cavity 17 via the gate or sprue (not shown) of the stationary or upper mold 11 and the gate or sprue 63.

A vent hole 18 is formed in the sink insert 16. The vent hole 18 is open to the cavity 17 at one end and connected to a feed tube 64 at the other end. The feed tube 64 is interposed between the movable or lower mold 12 and the stationary or upper mold 11 and connected to a gas feed unit 65 via a temperature control unit 66. A gas (e.g., air 9 compressed to a preselected pressure by the gas feed unit 65 and controlled to a preselected temperature by the temperature control unit 66) is fed via the feed tube 64.

In the illustrative embodiment, molten resin 20, heated above its softening point, is injected into the cavity 17 of the mold assembly 10 heated to a temperature lower than the softening point of the resin. Therefore, the temperature control unit 66 controls the gas to a temperature about 3° C. lower than the temperature of the mirror pieces or inserts 13 and 14 and reference insert 15. It follows that the temperature of the gas, fed from the feed tube 64 to the sink surface 16, is lower than the temperature of the mirror surfaces 22 and 23 and reference surface 25. The movable or lower mold 12 and the stationary or upper mold 11, surrounding the mirror inserts 13 and 14, the reference insert 15, and the sink insert 16, are each provided with a temperature control mechanism, including a heater and an oil cooler (not shown). The heater and oil cooler heat and cool, respectively, the associated molds 11 and 12, respectively, and therefore, the mirror inserts 13 and 14, the reference insert 15, and the sink insert 16.

In the illustrative embodiment, the temperature control unit 66 and gas feed unit 65 constitute a feeding device, and also constitute gas feeding means in combination with the vent hole 18.

The operation of the above-described arrangement will be discussed hereinafter. When a lens or similar plastic optical element is produced by conventional injection molding, molding conditions allowing the entire area to be transferred (i.e., allowing the internal pressure of the molding to drop substantially to zero at the time of take-out) are set up. However, because molten resin is sharply cooled as soon as it is introduced into a mold, the resulting temperature distribution, pressure distribution, density distribution and so forth disturb the shape of the molding. This, coupled with the internal strain (deflection) of the resin, adversely influences the optical characteristic of the molding. Although during the transfer of the mold configuration, internal strain and deformation may be reduced if a molding is caused to partly sink, it is extremely difficult to specify the part of a molding to sink. This embodiment is significant in that it can specify the part of a molding to sink, as follows.

While the mold assembly 10 is held at a temperature lower than the softening point of resin, molten resin 20, heated above its softening point, is injected into the cavity 17. Then, a resin pressure is caused to act on the transfer surfaces 13 a and 14 a of the mirror inserts 13 and 14, respectively. At the same time as the injection of the molten resin 20, a cool gas, compressed to a preselected pressure by the air feed unit 65 and controlled to a preselected temperature by the temperature control unit 66, is fed to the sink surface or B surface 24 via the vent hole 18. The feed of the gas, such as air, is continued until the molten resin 20 has been fully injected into the cavity 17. At this instant, the sink surface or B surface 24, lower in temperature than the mirror surfaces 22 and 23, solidifies first and increases its viscosity. This makes it difficult for the sink surface or B surface 24 to remain in contact with the non-transfer surface 16 a of the sink insert 16 before the end of the injection of the molten resin 20. After the injection of the molten resin 20 and the subsequent stop of the feeding of the cool gas, such as air, the cavity 17 is caused to dwell at a preselected pressure and cooled. As soon as the pressure inside the cavity 17 drops substantially to zero, the stationary or upper mold 11 is pulled away or separated from the movable or lower mold 12. Subsequently, the resulting molded article or product 21 is taken out of the cavity 17.

The sink surface or B surface 24 of the molded article or product 21 obtains a parting ability earlier than the other surfaces of the molded article or product 21. As a result, the sink surface or B surface 24 begins to sink earlier than the other surfaces (i.e., the mirror surfaces 22 and 23, and the reference or C surface 25) contacting the upper and lower mirror pieces or inserts 13 and 14, the reference insert 15, and the sink insert 16. This successfully prevents the mirror surfaces 22 and 23 from sinking and thereby allows the desired mirror surfaces 22 and 23 to be faithfully transferred to the molded article or product 21 in a short molding cycle.

Moreover, the sink surface or B surface 24 is held at a temperature lower than the temperature of the molten resin 20 from the end of the resin injection to the beginning of cooling. Consequently, a temperature difference does not occur between the mirror surfaces 22 and 23 and the sink surface or B surface 24 during cooling, so that an internal strain is prevented from remaining in the molded article or product 21 after the opening of the mold assembly 10. This not only prevents the accuracy of the mirror surfaces 22 and 23 from decreasing, but also prevents the entire molded article or product 21 from deforming.

In addition, the gas feeding means can be implemented only if the vent hole 18 is formed in the sink insert 16 and connected to both the temperature control unit 66 and gas feed unit 65. The mold assembly 10 is therefore simple in construction.

Sixteenth Embodiment

Referring to FIGS. 26, 27A-27D, and 28A-28D, a method and an apparatus for producing a plastic molded article or product 21 representative of a sixteenth embodiment of the present invention will be described. The molded srticle or product 21 to be provided by this embodiment is identical in configuration with the molded article or product 21 of the fifteenth embodiment and will be described with reference to FIGS. 23A-23C. Structural elements identical with the elements of the fifteenth embodiment are designated by identical reference numerals and will not be described specifically in order to avoid redundancy.

As shown in FIGS. 26 and 27A-27D, a plurality of (four in the embodiment) inserts are interposed between the movable or lower mold 12 and the stationary or upper mold 11 and constitute cavity inserts. Specifically, mirror pieces or inserts 13 and 14 face each other and are formed with transfer surfaces 13 a and 14 a, respectively, for forming the mirror surfaces 22 and 23, respectively, of the molded article or product 21. A reference insert 15 and a sink insert 16 face each other at both sides of the mirror pieces or inserts 13 and 14 and are formed with non-transfer surfaces 15 a and 16 a, respectively, in order to form the reference surface or C surface 25 and sink surface or B surface 24, respectively, of the molded article or product 21. The transfer and non-transfer surfaces 13 a, 14 a, 15 a, and 16 a of the mirror pieces or inserts 13 and 14, the reference insert 15, and the sink insert 16 form a cavity 17. The non-transfer surfaces 15 a and 16 a of the reference insert 15 and sink insert 16, respectively, are each formed with fine irregularities or undulations 62.

A gate or sprue (not shown) is formed in the stationary or upper mold 11, while a gate or sprue 63 is formed in the mirror insert 13 and is capable of communication with the gate or sprue (not shown) in the stationary or upper mold gate or sprue (not shown) of the stationary or upper mold 11 and the gate or sprue 63. A vent hole 18 is formed in the sink insert 16. The vent hole 18 is open to the cavity 17 at one end and connected to a feed tube 64 at the other end. The feed tube 64 is interposed between the movable or lower mold 12 and the stationary or upper mold 11.

The feed tube 64 is connected to a gas feed unit 65. The gas feed unit 65 feeds a gas, e.g., air 9 compressed to a preselected pressure, to between the sink surface 24 and the transfer surface 16 a of the sink insert 16, via the feed tube 64 and vent hole 18. In this embodiment, the gas feed unit 65 constitutes a feeding device and constitutes gas feeding means in combination with the vent hole 18 and feed tube 64.

The operation of the illustrative embodiment will be described with reference to FIGS. 27A-27D. As shown, while the mold assembly 10 is held at a temperature lower than the softening point of resin, molten resin 20, heated above its softening point, is injected into the cavity 17. Then, a resin pressure is caused to act on the transfer surfaces 13 a and 14 a of the mirror inserts 13 and 14, respectively. At the same time as the injection of the molten resin 20, a gas, i.e., air 9 compressed to a preselected pressure by the air feed unit 65, is fed to between the sink surface 16 a of the sink insert 16 and the non-transfer surface 15 a of the reference insert 15. The feed of the gas, e.g., air 9, is continued until the molten resin 20 has been fully injected into the cavity 17 (see FIGS. 27A and 27B). At this instant, a gas layer is formed between the non-transfer surface 16 a of the sink insert 16 and the sink surface 24 of the molded article or product 21, making it difficult for the sink surface 24 to remain in contact with the non-transfer surface 16 a of the sink insert 16 before the end of the injection of the molten resin 20.

After the injection of the molten resin 20 and the following stop of feed of the gas, e.g. air 9, the cavity 17 is caused to dwell at a preselected pressure and cooled. As a result, the gas layer between the sink surface or B surface 24 of the molded article or product 21 and the non-transfer surface 16 a of the sink insert 16 is compressed by the internal pressure of the molten resin 20, but remains between them (see FIG. 27C). Such residual gas expands as the internal pressure approaches zero, separating the sink surface or B surface 24 of the molded article or product 21 from the non-transfer surface 16 a of the sink insert 16. When the internal pressure reaches zero, the non-transfer surface 16 a of the sink insert 16 obtains a parting ability earlier than the other surfaces (i.e., transfer surfaces 13 a and 14 a of mirror pieces or inserts 13 and 14, respectively, and reference surface 15 a of reference insert 15). When the pressure inside the cavity 17 drops substantially to zero, the stationary or upper mold 11 is released from the movable or lower mold 12. Subsequently, the molded article or product 21 is taken out of the cavity 17.

In this manner, the sink surface or B surface 24 of the molded article or product 21 begins to sink earlier than the other surfaces (i.e., transfer surfaces 13 a, 14 a, and reference surface 15 a) contacting the mirror pieces or inserts 13 and 14 and the reference insert 15, respectively. This successfully prevents the mirror surfaces 22 and 23 of the molded article or product 21 from sinking and thereby allows the desired mirror surfaces 22 and 23 to be faithfully transferred to the molded article or product 21 in a short molding cycle. Moreover, the gas layer remains between the sink surface or B surface 24 of the molded article or product 21 and the non-transfer surface 16 a of the sink insert 16 until the cooling step begins after the injection of the molten resin 20, preventing the pressure difference, between the mirror surfaces 22 and 23 of the molded article or product 21 and the sink surface or B surface 24 of the molded article or product 21, from increasing during cooling. Consequently, the internal strain of the molded article or product 21 is prevented from remaining, after the opening of the mold assembly 10. This not only prevents the accuracy of the mirror surfaces 22 and 23 of the molded article or product 21 from decreasing, but also prevents the entire molded article or product 21 from deforming.

This embodiment may be practiced with the same configuration as the fifteenth embodiment, as follows. The gas fed from the gas feed unit 65 is controlled to substantially the same temperature as the mold assembly 10 by the temperature control unit 66 shown in FIG. 15. In this case, as shown in FIGS. 28A-28D, while the mold assembly 10 is held at a temperature lower than the softening point of resin, molten resin 20, heated above its softening point, is injected into the cavity 17. Then, a resin pressure is caused to act on the transfer surfaces 13 a and 14 a of the mirror pieces or inserts 13 and 14, respectively. At the same time as the injection of the molten resin 20, the gas, i.e., air 9 compressed to a preselected pressure by the gas feed unit 65, is fed to between the sink surface 24 of the molded article or product 21 and the non-transfer surface 16 a of the sink insert 16. The feed of the gas, e.g., air 9, is continued until the molten resin 20 has been fully injected into the cavity 17 (see FIGS. 28A and 28B). At this instant, a gas layer is formed between the non-transfer surface 16 a of the sink insert 16 and the sink surface 24 of the molded article or product 21, making it difficult for the sink surface 24 of the molded article or product 21 to remain in contact with the non-transfer surface 16 a of the sink insert 16 before the end of the injection of the molten resin 20.

After the injection of the molten resin 20 and the subsequent stop of feed of the gas, the cavity 17 is caused to dwell at a preselected pressure and cooled. As a result, the gas layer, between the sink surface 24 of the molded article or product 21 and the non-transfer surface 16 a of the sink insert 16, is compressed by the internal pressure of the molten resin 20, but remains between them (see FIG. 28C). The residual gas expands as the internal pressure approaches zero, separating the sink surface 24 of the molded article or product 21 from the non-transfer surface 16 a of the sink insert 16. When the internal pressure reaches zero, the non-transfer surface 16 a of the sink insert 16 obtains a parting ability earlier than the other surfaces, i.e., mirror surfaces 22 and 23 and reference or C surface 25 of the molded article or product 21 (see FIG. 28D). When the pressure inside the cavity 17 drops substantially to zero, the stationary or upper mold 11 is released from the movable or lower mold 12. Subsequently, the molded article or product 21 is taken out of the cavity 17.

Seventeenth Embodiment

A method and an apparatus for producing a plastic molded article or product 21 representative of a seventeenth embodiment of the present invention will be described with reference to FIGS. 29, 30A, and 30B. The molded article or product 21 to be produced by this embodiment is identical in configuration with the molded article or product 21 of the fifteenth embodiment and will be described in reference to FIGS. 23A-23C. Structural elements identical with the elements of the fifteenth embodiment will be designated by identical reference numerals and will not be described specifically in order to avoid redundancy.

As shown in FIGS. 29, 30A, and 30B, a plurality (four in the embodiment) of inserts, namely, mirror pieces or inserts 13 and 14, reference insert 15, and sink insert 16, are interposed between the movable or lower mold 12 and the stationary or upper mold 11 to form a cavity 17. Specifically, mirror pieces or inserts 13 and 14, which face each other across the cavity 17, are formed with transfer surfaces 13 a and 14 a, respectively, for forming the mirror surfaces 22 and 23, respectively, of the molded article or product 21 (see FIGS. 23A-23C). The reference insert 15 has a reference surface 15 a for forming a reference or C surface 25 on the molded article or product 21 and the sink insert 16 has a non-transfer surface 16 a for forming a sink or B surface 24 on the molded article or product 21. The surfaces 13 a, 14 a, 15 a, and 16 a of the inserts 13, 14, 15, and 16, respectively, form the cavity 17. The reference surface 15 a and the non-transfer 16 a of the reference insert 15 and the sink insert 16, respectively, are each formed with fine irregularities or undulations 62.

A gate or sprue (not shown) is formed in the stationary or upper mold 11, while a gate or sprue 63 is formed in the lower mirror piece or insert 14 of the movable or lower mold 12 and is capable of communication with the gate or sprue (not shown) of the stationary or upper mold 11. An injection molding machine (not shown) injects molten resin 20 into the cavity 17 via the gate or sprue (not shown) of the stationary or upper mold 11 and the gate or sprue 63 through the lower mirror piece or insert 14 formed in the movable or lower mold 12. A vent hole 18 is formed in the sink insert 16. One end of the vent hole 18 communicates with a gas feed unit 65 via a vent hole 18 formed in the movable or lower mold 12 and a feed tube 64. The other end of the vent hole 18 communicates with the outside of the mold assembly 10 via an exhaust tube 60.

The gas feed unit 65 feeds gas, e.g., air 9 controlled to a preselected pressure and a preselected temperature, to the vent hole 18, via the feed tube 64 and vent hole 18, and then discharges it via the vent hole 18 and exhaust tube 60. The gas, e.g., air 9 controlled to a preselected pressure and a preselected temperature, therefore cools the non-transfer surface 16 a of the sink insert 16 of the mold assembly 10.

In the illustrative embodiment, molten resin 20, heated above its softening point, is injected into the cavity 17 of the mold assembly 10 heated to a temperature lower than the softening point of the resin. Therefore, a temperature control unit 66 controls the temperature of the gas to a temperature about 3° C. lower than the temperature of the mirror pieces or inserts 13 and 14 and reference insert 15. It follows that the temperature of the gas, fed from the vent hole 18 to the sink surface or B surface 24 of the molded article or product 21, is lower than the temperature of the transfer surface 13 a and 14 a of the mirror pieces or inserts 13 and 14, respectively, and reference surface 15 a of the reference insert 15.

In this embodiment, the gas feed unit 65, feed tube 64, vent holes 18, 18, and 18, and exhaust tube 60 constitute cooling means.

In operation, before the injection of molten resin 20, a cool gas, e.g., air 9 controlled to a preselected pressure and a preselected temperature, is fed from the gas feed unit 65 to a non-transfer surface 16 a via the vent hole 18 so as to cool the non-transfer surface 16 a. Then, while the mold assembly 10 is held at a temperature lower than the softening point of resin, molten resin 20, heated above its softening point, is injected into the cavity 17. Subsequently, a resin pressure is caused to act on the transfer surfaces 13 a and 14 a of the mirror pieces or inserts 13 and 14, respectively. The feed of the cool gas, e.g., air 9, is continued until the molten resin 20 has been fully injected into the cavity 17. At this instant, the sink surface or B surface 24 of the molded article or product 21, lower in temperature than the mirror surfaces 22 and 23 of the molded article or product 21, solidifies first and increases its viscosity, making it difficult for the sink surface or B surface 24 to remain in contact with the non-transfer surface 16 a of the sink insert 16 before the end of the injection of the molten resin 20. After the injection of the molten resin 20 and the subsequent stop the of feeding of the cool gas, e.g., air 9, the cavity 17 is caused to dwell at a preselected pressure and cooled. When the pressure inside the cavity 17 drops substantially to zero, the stationary or upper mold 11 is released from the movable or lower mold 12. Subsequently, the molded article or product 21 is taken out of the cavity 17. This embodiment achieves the same advantages as the fifteenth embodiment.

Eighteenth Embodiment

A method and an apparatus for producing a plastic molded article or product 21 representative of a seventeenth embodiment of the present invention will be described with reference to FIGS. 31, 32A-32C, 33A, 33B, 34A-34C, and 35. The molded article or product 21 to be produced by this embodiment is identical in configuration with the molded article or product 21 of the fifteenth embodiment and will be described with reference to FIGS. 23A-23C. Structural elements identical with the elements of the fifteenth embodiment will be designated by identical reference numerals and will not be described specifically in order to avoid redundancy.

As shown, a plurality (four in the embodiment) of inserts, namely, mirror pieces or inserts 13 and 14, reference insert 15, and sink insert 16, are interposed between the movable or lower mold 12 and the stationary or upper mold 11 and form a cavity 17. Specifically, mirror pieces or inserts 13 and 14, which face each other across the cavity 17, are formed with mirror surfaces 13 a and 14 a, respectively, for forming the mirror surfaces 22 and 23, respectively, of the molded article or product 21. A reference insert 15 and a sink insert 16 face each other across the cavity 17 at both sides of the mirror pieces or inserts 13 and 14 and are formed with the transfer surface 15 and the non-transfer or sink surface 16 a, respectively, in order to form the reference surface or C surface 25 and the sink surface or B surface 25, respectively, of the molded article or product 21. The surfaces 13 a, 14 a, 15 a, and 16 a of the inserts 13, 14, 15, and 16, respectively, form the cavity 17. The reference surface 15 a and the non-transfer or sink surface 16 a of the reference insert 15 and the sink insert 16, respectively, are each formed with fine irregularities or undulations 62.

A gate or sprue (not shown) is formed in the mirror piece or insert 13 of the stationary or upper mold 11, while a gate or sprue 63 is formed in the mirror piece or insert 14 of the movable or lower mold 12 . The gate or sprue 63 formed in the lower mirror piece or insert 14 in the movable or lower mold 12 is capable of communication with the gate or sprue (not shown) of the stationary or upper mold 11. An injection molding machine (not shown) injects molten resin 20 into the cavity 17 via the gate or sprue (not shown) of the stationary or upper mold 11 and the gate or sprue 63. A vent hole 18 is formed in the sink insert 16. The vent hole 18 is open to the cavity 17 at one end and connected to a bore 19 at the other end. The bore 19 communicates with a flow rate control unit 67 via a vent hole 18, formed in the movable or lower mold 12, and a feed tube 64. The flow rate control unit 67 is connected to a gas feed unit 65 via both a pressure control unit 68 and a temperature control unit 66.

The gas feed unit 65 constitutes a gas source. The temperature control unit 66 controls the temperature of a gas, such as air 9, fed from the gas feed unit 65. The pressure control unit 68 controls the pressure of the gas fed from the gas feed unit 65. Further, the flow rate control unit 67 controls the flow rate of the gas, such as air 9, fed from the gas feed unit 65. The vent hole 18 communicates with an exhaust valve 69 via a vent hole 18, formed in the movable or lower mold 12, and an exhaust tube 60. The gas, such as air 9, fed from the gas feed unit 65 to the vent hole 18 is either discharged to the outside, when the exhaust valve 69 is open, or is introduced into the cavity 17, when the exhaust valve 69 is closed.

In this embodiment, the flow rate control unit 67, pressure control unit 68, temperature control unit 66, and gas feed unit 65 constitute a feeding device. The feeding device constitutes gas feeding means in combination with the vent holes 18, 18, 18, and 18, feed tube 64, and exhaust valve 69.

The operation of the illustrative embodiment will be described with reference to FIGS. 33A, 33B, and 34A-34C. Briefly, this embodiment is characterized in that a step of pressing the sink surface or B surface 24 of the molded article or product 21 of molten resin 20 with the gas, e.g., air 9, is combined with at least one of a step of lowering the temperature of the sink surface or B surface 24 of the molded article or product 21 below the temperature of the mirror surfaces 22 and 23 of the molded article or product 21, a step of forming a gas layer between the sink surface or B surface 24 of the molded article or product 21 and the sink insert 16, and a step of lowering the temperature of the sink insert 16 facing the sink surface or B surface 24 of the molded article or product 21 below the temperature of the mirror inserts 13 and 14. The following description will concentrate on the combination of all of such steps.

First, the exhaust valve 69 is opened to feed a small amount of gas, e.g., air 9, to the vent hole 18 via the flow rate control unit 67, thereby cooling the sink insert 16 (see FIG. 33A). Specifically, the flow rate of the gas, e.g., air 9, is selected so as to prevent the gas from entering the cavity 17. Otherwise, the gas, e.g., air 9, would enter the cavity 17 and cool even the mirror surfaces 13 and 14. If desired, the temperature of the gas may be controlled in order to promote the effective cooling of the sink insert 16.

After the mold assembly 10 has been heated to a temperature lower than the softening point of resin, but before molten resin 20, heated to a temperature above its softening point, is injected into the cavity 17, the flow rate unit 67 and pressure control unit 68, respectively. As a result, the gas, e.g., air 9, is admitted into the cavity 17. Subsequently, the molten resin 20 begins to be injected into the cavity 17 (see FIG. 33B). The increase in the flow rate of the gas, e.g., air 9, promotes the cooling of the molten resin 20, while the increase in the pressure of the gas allows the gas to press the sink surface or B surface 24 of the molded article or product 21 and the sink insert 16.

After the injection of the molten resin 20 (see FIG. 34A), the exhaust valve 69 is closed, while the pressure of the gas, e.g., air 9, is adequately controlled by the pressure control unit 68. As a result, the cavity 17 is caused to dwell at a preselected pressure and cooled (see FIGS. 34B and 34C). When the pressure inside the cavity 17 drops substantially to zero, the stationary or upper mold 11 is released from the movable or lower mold 12. Thereafter, the molded article or product 21 is taken out of the cavity 17.

This embodiment achieves the same advantages as the fifteenth embodiment, and in addition, achieves an advantage that the sink surface or B surface 24 of the molded article or product 21 is constantly pressed and therefore, easily separates from the sink insert 16. This allows the sink surface or B surface 24 of the molded article or product 21 to sink more positively.

FIG. 35 shows an alternative arrangement, wherein the flow control unit 67 is connected to a gas conduit work 70 available in a factory.

Constantly pressing the sink surface or B surface 24 of the molded article or product 21, as shown and described, is not essential. Alternatively, at least one of three different methods may be used, as follows: lowering the temperature of at least one of the non-transfer surfaces of the molten resin below the temperature of the transfer surfaces from the beginning to the end of the injection of the molten resin; forming a gas layer between at least one of the non-transfer surfaces of the molten resin and the mold assembly; and lowering the temperature of the mold portion facing at least one of the non-transfer surfaces of the molten resin below the temperature of the mold portion facing the transfer surfaces.

The fifteenth to eighteenth embodiments, shown and described above, have the following unprecedented advantages.

(1) The non-transfer surface of a molded article or product obtains a parting ability earlier than the other surfaces of the same. This successfully prevents the transfer surfaces of the molded article or product from sinking and thereby allows desired mirror surfaces to be faithfully transferred to the molded article or product in a short molding cycle.

(2) The non-transfer surface of molten rein is held ta a temperature lower than the temperature of the transfer surfaces from the end of resin injection to the beginning of cooling. Consequently, a temperature difference does not occur between the transfer surfaces and the non-transfer surfaces during cooling, so that an internal strain is prevented from remaining in the molded article or product after the opening of the mold assembly. This not only prevents the accuracy of the transfer surfaces from decreasing, but also prevents the entire molded article or product from deforming.

(3) A gas layer is formed between the non-transfer surface of the resin and the mold assembly until the cooling step begins after the injection of the molten resin, preventing the pressure difference between the transfer surfaces and the non-transfer surface from increasing during cooling. Consequently, the internal strain of the molded article or product is prevented from remaining after the opening of the mold assembly. This not only prevents the accuracy of the transfer surfaces from decreasing, but also prevents the entire molded article or product from deforming.

(4) The gas layer is formed between the non-transfer surfaces of the resin and the mold assembly, and/or the temperature of the non-transfer surface, until the cooling step begins after the injection of the molten resin, thereby preventing a difference in temperature or pressure between the transfer surface and the non-transfer surface from increasing during cooling. Consequently, the internal strain of the molded article or product is prevented from remaining after the opening of the mold assembly. This not only prevents the accuracy of the transfer surfaces from decreasing, but also prevents the entire molded article or product from deforming.

(5) The temperature of the non-transfer surface of the resin is lowered, the non-transfer surface is pressed, and/or the gas layer is formed between the non-transfer surface of the resin and the mold assembly. This allows the non-transfer surface to sink with priority by use of a simple construction.

(6) Gas feeding means can be implemented only if a vent hole is formed in the mold assembly and communicates with a feeding device. This prevents the configuration of the mold assembly from being complicated.

(7) By cooling the non-transfer surface of the mold assembly with cooling means, it is possible to cool the non-transfer surface of the resin. The non-transfer surface can therefore be caused to sink by an inexpensive construction of the mold assembly.

Various modifications will become possible for those skilled in the art after receiving the teachings of the present disclosure without departing from the scope thereof. For example, while the embodiments have concentrated on a molded article or product in the form of a rectangular lens (having two mirror surfaces or optical surfaces), the present invention is similarly applicable to, e.g., a mirror having a single mirror surface or a prism having a plurality of mirror surfaces. 

What is claimed is:
 1. A lens comprising: a bottom base surface; front and rear end surfaces extending upwardly from the bottom base surface; front and rear shoulder surfaces extending inwardly from the front and rear end surfaces, respectively, so as to oppose each other; an arcuate top surface extending from an inner edge of the front shoulder surface to an inner edge of the rear shoulder surface; left and right side surfaces extending perpendicular to the front and rear end surfaces, respectively; and at least one projection extending outwardly from the right side surface.
 2. The lens according to claim 1, wherein the at least one projection is first and second projections extending parallel to one another.
 3. The lens according to claim 2, wherein the first and second projections extend in a longitudinal direction of the right side surface, are shorter in length than a length of the arcuate top portion, and are longer in length than one-half of a length of the right and left side surfaces.
 4. The lens according to claim 2, further comprising a sunken portion between the first and second projections.
 5. The lens according to claim 1, wherein the at least one projection is a single projection circumscribing a rectangular configuration.
 6. The lens according to claim 5, wherein the projection has two long side portions extending in a longitudinal direction of the right side surface and two short side portions extending in a heighth direction of the right side surface, the two long side portions being shorter in length than a length of the arcuate top portion and longer in length than one-half of a length of the right and left side surfaces.
 7. The lens according to claim 6, further comprising a sunken portion located between the two long side portions and the two short side portions of the projection.
 8. The lens according to claim 1, wherein the at least one projection is a single projection including an upper arcuate portion extending parallel to an edge of the arcuate top surface and a lower linear portion extending parallel to an edge of the bottom base surface, the lower linear portion connecting ends of the upper arcuate portion.
 9. The lens according to claim 8, further comprising a sunken portion located between the upper arcuate portion and the lower linear portion of the projection.
 10. A lens comprising: a bottom base surface; front and rear end surfaces extending upwardly from the bottom base surface; front and rear shoulder surfaces extending inwardly from the front and rear end surfaces, respectively, so as to oppose each other; an arcuate top surface extending from an inner edge of the front shoulder surface to an inner edge of the rear shoulder surface; left and right side surfaces extending perpendicular to the front and rear end surfaces, respectively; and at least one indentation extending into the right side surface.
 11. The lens according to claim 10, wherein the at least one indentation is first and second indentations extending parallel to one another.
 12. The lens according to claim 11, wherein the first and second indentations extend in a longitudinal direction of the right side surface, are shorter in length than a length of the arcuate top portion, and are longer in length than one-half of a length of the right and left side surfaces.
 13. The lens according to claim 12, further comprising a sunken portion between the first and second indentations.
 14. The lens according to claim 10, wherein the at least one indentation is a single indentation circumscribing a rectangular configuration.
 15. The lens according to claim 14, wherein the indentation has two long side portions extending in a longitudinal direction of the right side surface and two short side portions extending in a heighth direction of the right side surface, the two long side portions being shorter in length than a length of the arcuate top portion and longer in length than one-half of a length of the right and left side surfaces.
 16. The lens according to claim 15, further comprising a sunken portion located between the two long side portions and the two short side portions of the indentation.
 17. The lens according to claim 10, wherein the at least one indentation is a single indentation including an upper arcuate portion extending parallel to an edge of the arcuate top surface and a lower linear portion extending parallel to an edge of the bottom base surface, the lower linear portion connecting ends of the upper arcuate portion.
 18. The lens according to claim 17, further comprising a sunken portion located between the upper arcuate portion and the lower linear portion of the indentation.
 19. A lens comprising: a bottom base surface; front and rear end surfaces extending upwardly from the bottom base surface; front and rear shoulder surfaces extending inwardly from the front and rear end surfaces, respectively, so as to oppose each other; an arcuate top surface extending from an inner edge of the front shoulder surface to an inner edge of the rear shoulder surface; left and right side surfaces extending perpendicular to the front and rear end surfaces, respectively; and at least one projection extending from an edge of at least one of the left and right side surfaces.
 20. The lens according to claim 19, wherein the at least one projection is upper and lower projections, the upper projection extending upwardly from an edge of the arcuate top surface between the inner edges of the front and rear shoulder surfaces and the lower projection extending downwardly from an edge of the bottom base surface between the inner edges of the front and rear shoulder surfaces.
 21. The lens according to claim 20, further comprising a sunken portion located between the upper and lower projections.
 22. The lens according to claim 20, wherein the upper and lower projections are either square-shaped or rectangular-shaped in cross-section.
 23. The lens according to claim 19, wherein the at least one projection is a single projection extending upwardly from an edge of the arcuate top surface.
 24. The lens according to claim 23, wherein the projection is shorter in length that a length of the arcuate top surface and spans an approximate middle portion of the arcuate top surface.
 25. The lens according to claim 23, further comprising a sunken portion located below the projection and sunken into the right side surface.
 26. The lens according to claim 19, wherein the at least one projection is left and right upper projections and left and right lower projections, the left and right upper projections extending upwardly from left and right edges, respectively, of the arcuate top surface between the inner edges of the front and rear shoulder surfaces, and the left and right lower projections extending downwardly from left and right edges, respectively, of the bottom base surface between the inner edges of the front and rear shoulder surfaces.
 27. The lens according to claim 26, further comprising a sunken portion located between the right upper and lower projections and sunken into the right side surface.
 28. The lens according to claim 26, wherein the right and left upper projections and the right and left lower projections are all either square-shaped or rectangular-shaped in cross-section.
 29. The lens according to claim 19, wherein the at least one projection is upper and lower projections both circumscribing a rectangular configuration.
 30. The lens according to claim 29, wherein: the upper projection includes left and right long side portions and front and rear short side portions, the left and right long side portions extending upwardly from left and right edges, respectively, of the arcuate top surface and the front and rear short side portions extending upwardly from front and rear edges, respectively, of the arcuate top surface; and the lower projections includes left and right long side portions and front and rear short side portions, the left and right long side portions extending downwardly from left and right edges, respectively, of the bottom base surface and the front and rear short portions extending downwardly from front and rear edges, respectively, of the bottom base surface.
 31. The lens according to claim 30, wherein the upper and lower projections are both either square-shaped or rectangular-shaped in cross-section.
 32. The lens according to claim 30, wherein the upper and lower projections are both triangular-shaped in cross-section.
 33. The lens according to claim 30, wherein the upper and lower projections both have a cross-sectional shape in which a first curved side has first and second ends thereof connected to two linear sides, the two linear sides being connected to each other at a right angle to each other so that the cross-sectional shape of the upper and lower projections is somewhat the shape of a quadrant or one-quarter of a circle.
 34. The lens according to claim 30, wherein the upper and lower projections both have a cross-section in the shape of a quadrilateral having two opposing sides parallel to each other and another two opposing sides which are not parallel to each other.
 35. The lens according to claim 30, further comprising a sunken portion located between the right long portion of the upper projection and right long side portion of lower projection and sunken into the right side surface of the lens. 